Jiande Yitong Metal Powder Co.,Ltd

300W series water atomized iron powder has excellent performance and is proved to reach the same quality level as the same imported powder. This product has been wide accepted by customers.

Partially Alloyed Steel Powder For High Strength Applications(2300WB)
Properties of Powder

Chemical Composition%	Ni	4	Cu	1.5	Mo	0.5
Apparent Density g/cm3		2.98	Compressibility* g/cm3	500MPa 6.90
Flow Rate s/50g		26.9	Compressibility* g/cm3	600Mpa 7.05
Particle Size Distribution	-180+250	-150+106	-106+75	-75+63	-63+45	-45
Particle Size Distribution	0.5	22.5	21	12	19	25

*mixed with 0.75%Zn-St
Characteristics:1)High Compressibility ;2)The sintering atmosphere is changeable to demand as adding Ni.3)It can reach higher intensity and hardness without heat treatment;4)Sintering temperature can be controlled according to intensity demand. Applications:1) Auto sintered parts such as clutch gear, oil pump washer;2)other sintered mechanical components.

Partially Alloyed Steel Powder For High Strength Applications(1300WB) Mechanical Properties of Powder After Sintering
Properties of Powder

Chemical Composition%	Ni	2	Cu	1.5	Mo	0.5
Apparent Density g/cm3		2.98	Compressibility* g/cm3	500MPa 6.93
Flow Rate s/50g		26.9	Compressibility* g/cm3	600Mpa 7.10
Particle Size Distribution	-180+250	-150+106	-106+75	-75+63	-63+45	-45
Particle Size Distribution	0.5	22.5	21	12	19	25

*mixed with 0.75%Zn-St
Characteristics:1)High Compressibility ;2)The sintering atmosphere is changeable to demand as adding Ni.3)It can reach higher intensity and hardness without heat treatment
Applications:1)Auto parts such as gear 2)other sintered mechanical components.

Completely Alloyed Steel Powder For High Strength Applications(1300WA) Mechanical Properties of Powder After Sintering
Properties of Powder

Chemical Composition%	Ni	1.7-2.2	Mo	0.4-0.6
Apparent Density g/cm3		2.98	Compressibility* g/cm3	500MPa 6.73
Flow Rate s/50g		26.5	Compressibility* g/cm3	600Mpa 6.94
Particle Size Distribution	-180+250	-150+106	-106+75	-75+63	-63+45	-45
Particle Size Distribution	0.5	22.5	21	12	19	25

*mixed with 0.75%Zn-St
Characteristics:1) High Quenching Degree2)It can reach higher intensity and without heat treatment
Applications:1)Auto parts 2)Medium-high density sintered structural parts

300W Water Atomized Pure Iron Powder Sintered Material

Properties

Code Name（MPIF Standard）	Composition of Mixed Powde（%）					Sintering Density（g/cm3)	Dimensional Change 1) Rate（%）	Transverse Rupture Strength（MPa）	Extreme Tensile Strength（MPa）	Yield Strength（MPa）	Tensile Ratio%	Apparent Hardness HRB
Code Name（MPIF Standard）	Fe	Cu	Ni	Graphite	Zinc Stearate	Sintering Density（g/cm3)	Dimensional Change 1) Rate（%）	Transverse Rupture Strength（MPa）	Extreme Tensile Strength（MPa）	Yield Strength（MPa）	Tensile Ratio%	Apparent Hardness HRB
Sintered Carbon Steel
F-0000	Balance	-	-	0.0	0.5	6.8	-0.06	445	205	141	10	27
	Balance	-	-	0.0	0.5	7.0	-0.04	535	230	152	13	37
	Balance	-	-	0.3	0.5	6.8	+0.02	493	243	170	7	38
	Balance	-	-	0.3	0.5	7.0	+0.07	610	276	186	9	46
F-0005	Balance	-	-	0.6	0.5	6.8	+0.09	635	305	221	4	55
F-0005	Balance	-	-	0.6	0.5	7.0	+0.13	722	342	237	5	61
F-0008	Balance	-	-	0.9	0.5	6.8	+0.14	737	359	264	3	68
F-0008	Balance	-	-	0.9	0.5	7.0	+0.17	826	405	285	3	74
Sintered Copper Steel
FC-0200	Balance	2.0	-	0.0	0.5	6.8	+0.56	661	248	145	3	56
FC-0200	Balance	2.0	-	0.0	0.5	7.0	+0.58	745	276	165	5	63
FC-0205	Balance	2.0	-	0.6	0.5	6.8	+0.39	944	455	358	2	80
FC-0205	Balance	2.0	-	0.6	0.5	7.0	+0.42	1096	503	386	3	86
FC-0208	Balance	2.0	-	0.9	0.5	6.8	+0.22	1082	538	448	2	88
FC-0208	Balance	2.0	-	0.9	0.5	7.0	+0.30	1255	600	489	2	92
Sintered Nickel Steel
FN-0200	Balance	-	2.0	0.3	0.5	6.8	-0.12	634	269	159	2	49
FN-0200	Balance	-	2.0	0.3	0.5	7.0	-0.09	717	303	165	5	55
FN-0205	Balance	-	2.0	0.6	0.5	6.8	-0.07	717	303	214	2	64
FN-0205	Balance	-	2.0	0.6	0.5	7.0	-0.01	841	372	234	3	67
FN-0208	Balance	-	2.0	0.9	0.5	6.8	+0.02	807	352	290	1	73
FN-0208	Balance	-	2.0	0.9	0.5	7.0	+0.07	965	421	317	1	79
FN-0405	Balance	-	4.0	0.6	0.5	6.8	-0.11	820	296	255	<1	77
FN-0405	Balance	-	4.0	0.6	0.5	7.0	-0.06	1007	379	290	1	81
FN-0408	Balance	-	4.0	0.9	0.5	6.8	-0.10	800	303	283	<1	78
FN-0408	Balance	-	4.0	0.9	0.5	7.0	-0.14	1000	400	331	<1	84

Sintering in an atmosphere of endothermal coal gas for 35 minutes at 1120°C 。
¹⁾Dimensional change is from sintered die size.

300W Water Atomized Pure Iron Powder Sintered Material Properties after Heat Treating

Code Name（MPIF Standard）	Composition of Mixed Powder（%）					Sintering Density（g/cm3)	Transverse Rupture Strength（MPa）	Extreme Tensile Strength（MPa）	Impact Strength（Ｊ）	Apparent Hardness HRB
Code Name（MPIF Standard）	Fe	Cu	Ni	Graphite	Zinc Stearate	Sintering Density（g/cm3)	Transverse Rupture Strength（MPa）	Extreme Tensile Strength（MPa）	Impact Strength（Ｊ）	Apparent Hardness HRB
Sintered Copper Steel^1）
FC-0205HT	Balance	2.0	-	0.6	0.5	6.8	1172	789	-	27
	Balance	2.0	-	0.6	0.5	7.0	1344	869	-	30
	Balance	3.0	-	0.6	0.5	6.8	1234	765	-	27
	Balance	3.0	-	0.6	0.5	7.0	1372	882	-	29
FC-0208HT	Balance	2.0	-	0.9	0.5	6.8	1358	862	-	35
	Balance	2.0	-	0.9	0.5	7.0	1593	1027	-	40
	Balance	3.0	-	0.9	0.5	6.8	1434	848	-	34
	Balance	3.0	-	0.9	0.5	7.0	1744	979	-	38
Sintered Nickel Steel^2）
FN-0205HT	Balance	-	2.0	0.6	0.5	6.8	1158	885	8	37
FN-0205HT	Balance	-	2.0	0.6	0.5	7.0	1358	1013	8	42
FN-0405HT	Balance	-	4.0	0.6	0.5	6.8	1200	834	9	26
FN-0405HT	Balance	-	4.0	0.6	0.5	7.0	1462	965	12	31

Sintering in an atmosphere of endothermal coal gas for 30 minutes at 1120°C.
奥氏体化Heat Treating: for 15minutes at 845°C .
^1） Oil Quenching, tempering for 60 minutes at 175°C.
^2）Oil Quenching, tempering for 60 minutes at 260°C.