Water Atomized Iron Powder Material：

Category
　
Designation
Chemical Composition （%）
Particle Size Distribution （μm）
Apparent
Density
g/cm3
Flow
Rate
s/50g

Compressibility

g/cm3  0.75%Zn-St  490.3MPa
Rattler Value%0.75%Zn-St 490.3MPa

C
Si
Mn
P
S
Cu
Ni
Mo
W
V
Co
Cr
[O]
HCL Undissolved
Fe
250-180
180-150
150-106
106-75
75-63
63-45
-45

Pure Iron Powder
　
300W

<0.02
<0.05
<0.30
<0.02
<0.02
-
-
-
-
-
-
-
<0.20
<0.15
 Balance
<1
<10
10-25
15-30
5-20
8-23
20-40
2.85-3.05
<30
>6.85
<1.0
300WH
<0.01
<0.03
<0.10
<0.01
<0.01
<0.05
<0.05
-
-
-
-
-
<0.15
<0.10
Balance
<1
<10
10-25
15-30
5-20
8-23
15-35
2.85-3.05
<30
>6.90
<1.0
270W
<0.02
<0.05
<0.30
<0.02
<0.02
-
-
-
-
-
-
-
<0.20
<0.15
Balance
<10
<10
10-31
18-33
5-20
5-20
9-30
2.60-2.80
<30
>6.80
<0.8
Low
Alloy

Steel

Powder
　
Pre-alloyed
1300WA
<0.02
<0.05
<0.30
<0.03
<0.02
-
1.70-2.20
0.40-0.60
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
20-40
2.85-3.10
<30
>6.70
<1.5
5300WA
<0.02
<0.05
<0.30
<0.03
<0.02
-
1.40-1.60
0.90-1.10
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
20-40
2.85-3.10
<30
>6.70
<1.5
7300WA
<0.01
<0.05
0.45-0.80
<0.02
<0.02
-
0.80-1.20
0.90-1.20
-
-
-
0.40-0.55
<0.25
<0.15
Balance
<10
<15
10-30
15-35
5-25
5-25
10-30
2.85-3.05
<30
>6.6
<1.0
9270WA
<0.01
<0.05
0.10-0.30
<0.02
<0.02
-
-
0.20-0.40
-
0.20-0.40
-
2.50-3.30
<0.25
<0.15
Balance
<10
<15
10-30
15-35
5-25
5-25
10-30
2.50-2.90
<30
>6.5
<1.0
Diffusion
2300WB
<0.02
<0.05
<0.20
<0.02
<0.02
1.30-1.70
3.60-4.40
0.40-0.60
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
20-40
2.85-3.10
<30
>6.85
<1.0
4300WB
<0.02
<0.05
<0.20
<0.02
<0.02
1.30-1.70
5.0-7.0
0.80-1.20
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
20-40
2.85-3.10
<30
>6.85
<1.0
Easy Cutting Steel Powder
300WSA
<0.02
<0.05
0.10-0.30
<0.02
0.28-0.40
-
-
-
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
15-35
2.75-3.05
<30
>6.70
<1.0
300WSB
<0.02
<0.05
0.50-0.80
<0.04
0.30-0.35
-
-
-
-
-
-
-
<0.20
<0.15
Balance
<1
<10
10-25
15-30
5-20
8-23
15-35
2.75-3.10
<30
>6.65
<1.0

Stainless

Steel

 Powder
304L
<0.02
0.8
0.2
-
-
-
11.5-12.5
-
-
-
-
17.5-18.5
<0.20
-
Balance
-
<1
6-15
15-30
5-20
10-30
20-45
2.6-3.0
<30
>6.551）
-
316L
<0.02
0.7
0.2
-
-
-
12.0-14.0
2.0-2.50
-
-
-
17.5-18.5
<0.20
-
Balance
-
<1
6-15
15-30
5-20
10-30
20-45
2.6-3.0
<30
>6.601）
-
410L
<0.02
0.8
0.5
-
-
-
-
-
-
-
-
11.5-13.0
<0.20
-
Balance
-
<1
6-15
15-30
5-20
8-30
20-45
2.8-3.1
<30
>6.601）
-
430L
<0.02
0.8
0.2
-
-
-
-
-
-
-
-
17.5-18.5
<0.25
-
Balance
-
1-3
6-15
12-25
5-20
10-25
30-55
2.7-3.0
<30
>6.451）
-
434L
<0.02
0.8
0.2
-
-
-
-
1
-
-
-
17.5-18.5
<0.25
-
Balance
-
1-3
6-15
12-25
5-20
10-25
30-55
2.7-3.0
<30
>6.401）
-

High Alloy Steel Powder
　

2260WG
1.0
-
-
-
-
-
-
5
6
2
-
4
<0.15
-
Balance
-
<1
6-15
12-25
5-20
5-20
15-35
2.3-2.6
<30
>6.401）
-
4260WG
1.3
-
-
-
-
-
-
3
9
3
10
4
<0.15
-
Balance
-
<1
6-15
12-25
5-20
5-20
15-35
2.3-2.6
<30
>6.151）
-
6300WG
-
2.6
-
-
-
-
-
30
-
-
-
9
<0.15
-
Balance
-
<1
6-15
12-25
5-20
5-20
15-35
2.8-3.2
<30
-
-

Iron Powder for Welding Rod
　
FHT40·30
<0.02
<0.10
<0.40
<0.02
<0.02
-
-
-
-
-
-
-
<0.50
-
>98.0
+425<1%,    250-425    5-20%(其中FHT40·37    5-30%),106-250  Balance,    -106<20%
2.9-3.1
<32
-
-
FHT40·37
<0.02
<0.10
<0.40
<0.02
<0.02
-
-
-
-
-
-
-
<0.50
-
>98.0
3.6-3.8
<30
-
-
FHT100·25
<0.02
<0.10
<0.40
<0.02
<0.02
-
-
-
-
-
-
-
<0.50
-
>98.0
-
≤5
10-35
Balance
≤20
2.4-2.6
<36
-
-

Iron Powder for Magnetism
　
260WC
<0.01
<0.03
<0.15
<0.02
<0.02
<0.05
<0.05
-
-
-
-
<0.05
<0.15
<0.10
Balance
<10
<10
15-30
15-30
5-20
5-20
10-30
2.4-2.8
<30
>6.85
<0.8
300WC
<0.01
<0.03
<0.15
<0.02
<0.01
<0.05
<0.05
-
-
-
-
<0.05
<0.15
<0.10
Balance
<10
<10
15-30
15-30
5-20
5-20
5-25
2.85-3.05
<30
>6.90
<1.0
Super-fine Iron Powder
200Mesh
<0.02
<0.05
<0.30
<0.02
<0.02
-
-
-
-
-
-
-
<0.25
<0.20
Balance
106-75    <3%      -75    Balance
2.8-3.30
-
-
-
325Mesh
<0.02
<0.05
<0.30
<0.02
<0.02
-
-
-
-
-
-
-
<0.30
<0.20
Balance
75-45     <3%      -45    Balance
2.8-3.30
-
-
-
Ni Powder
200Mesh
-
-
-
-
-
-
>99.5
-
-
-
-
-
-
-
-
106-75    <3%      -75    Balance
2.7-3.20
-
-
-
325Mesh
-
-
-
-
-
-
>99.2
-
-
-
-
-
-
-
-
75-45     <3%      -45    Balance
2.7-3.20
-
-
-
1）Compacting Pressure 600MPa,1%Zn-St

Copper-based Alloy Powder：
Category
Designation
Chemical Composition （%）
Particle Size Distribution   （μm）(%)
Apparent
Density（g/cc）
Flow
Rate（s/50g）
Green
Density
165MPa(N/mm2)
Cu
Sn
Zn
Pb
Fe<
Ni<
Sb<
P<
O<
Impurity<
+80
+100
+150
+200
+250
+325
-325
Sintered CuPb
Alloy Powder　
　
JWCu24-1
Balance
0.2-1.5
<0.25
23.0-27.0
0.25
0.5
0.25
0.03
0.3
(other)0.25
<0.1
<1.0
2.0-12.0
10.0-20.0
5.0-20.0
5.0-25.0
35.0-55.0
>5.0
<15
-
JWCu10-10
Balance
9.5-11.0
<0.5
9.5-11.0
0.15
0.5
0.25
0.03
0.03
(other)0.25
<0.1
<0.1
2.0-12.0
10.0-20.0
5.0-20.0
5.0-25.0
35.0-55.0
3.8-5.2
<25 
-
JWCu25-5
Balance
4.5-5.5
<0.25
23.0-27.0
0.25
0.5
0.25
0.03
0.03
(other)0.25
<0.1
<0.1
2.0-12.0
10.0-20.0
5.0-20.0
5.0-25.0
35.0-55.0
>5.0

<15 
- 
JWCu7-7-7
Balance
6.0-8.0
6.0-8.0

2.0-4.0
0.25
0.5
0.25
0.03
0.03
(other)0.25
<0.1
<0.1
2.0-12.0
10.0-20.0
5.0-20.0
5.0-25.0
35.0-55.0
3.8-5.2
<25
-
High-strength
Copper

Powder
　
JGCu180
>99.8
 　
-
-
-
-
-
-
-
0.03
0.2
-
-
-
<1.0
<3.0
<0.5
Balance
1.6-2.0

-
>15
JGCu220
>99.8
-
-
-
-
-
-
-
0.03
0.2
-
-
-
<1.0
5.0-15.0
5.0-15.0
Balance
2.0-2.5
<45
>9.0
JGCu270
99.8
-
-
-
-
-
-
-
0.03
0.2
-
-
<3.0
1.0-5.0
5.0-20.0
5.0-25.0
25.0-40.0
2.5-2.9
<35
>8.0
Sn-Bronze
Alloy

Powder
　
JHCu280
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
5.0-15.0
5.0-15.0
10.0-20.0
8.0-15.0
15.0-30.0
2.7-2.9
<35
-
JHCu300
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
5.0-15.0
5.0-15.0
10.0-25.0
10.0-20.0
20.0-40.0
2.9-3.1
<35
-
JHCu320
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
3.0-10.0
5.0-15.0
10.0-20.0
15.0-25.0
20.0-50.0
3.1-3.3
<35
-
Sn-Bronze
Mixed

Powder
　
JXCu260
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
10.0-20.0
10.0-20.0
15.0-25.0
10.0-20.0
20.0-35.0
2.5-2.7
<35
-
JXCu280
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
8.0-20.0
10.0-20.0
10.0-20.0
15.0-25.0
30.0-50.0
2.7-2.9
<35
-
JXCu300
Balance
9.5-11.0
-
-
-
-
-
-
0.03
0.2
-
<0.1
2.0-10.0
3.0-10.0
10.0-20.0
15.0-30.0
40.0-60.0
2.9-3.1
<35
-
Atomized

Bronze

Powder
　
JPCu6-6-3
Balance
5.0-7.0
5.0-7.0
2.0-4.0
-
-
-
-
0.03
0.3
+80<1.0%    -80~+200    50~80%    -200<50%
2.6-3.5
<35
-
JPCu663
Balance
5.0-7.0
5.0-7.0
2.0-4.0
-
-
-
-
0.03
0.3
-
-
-
<3.0
5.0-20.0
10.0-30.0
40.0-80
3.5-4.5
-
-
Atomized Copper
Powder
　
JFCu80
99.8
-
-
-
-
-
-
-
0.03
0.2
+80<1.0%    -80~+200    50~80%    -200<50%
2.6-3.5
<35
-
JFCu200
99.8
-
-
-
-
-
-
-
0.03
0.2
-
-
-
<3.0
5.0-20.0
10.0-30.0
40.0-80
3.2-4.2
-
-
JFCu325
99.8
-
-
-
-
-
-
-
0.03
0.2
-
-
-
-
<1.0
<5.0
Balance
2.8-3.5
-